Nickel welding Wire ERNiCu-7 Monel 400/K500 welding wire
ErNicu-7 （Monel 400/K500）Welding Wire
♦ Welding Material Name: Nickel welding Wire, ErNiCu-7, Monel 400/K500 Welding Wire
♦ MOQ:15kg
♦ Form: MIG(15kgs/spool), TIG(5kgs/box)
♦ Size: Diameter 0.01mm-8.0mm
♦ Common Size： 0.8MM / 1.0MM / 1.2MM / 1.6MM / 2.4MM / 3.2MM / 3.8MM / 4.0MM / 5.0MM
♦ Standards: Conforms to Certification AWS A5.14 ASME SFA A5.14
ErNiCu-7 Based Material is Monel 400 and Monel K500, This welding wire is mainly used for welding MONEL400 alloy, MONELR404 alloy and MOENLK-500 alloy by tungsten inert-gas welding, MGW and submerged arc welding, and can also be used for surfacing steel surface welding by MGW and submerged arc welding.
It is recommended to use the Erni-1 nickel wire cover for specific gas welding conditions.
|
C |
Al |
Ni |
Si |
Mn |
P |
S |
Fe |
Cu |
Ti |
Other |
|
≤0.15 |
≤1.25 | 62.0-69.0 | ≤1.25 | ≤4.0 | ≤0.02 | ≤0.015 | ≤2.5 | Bal | 1.5-3.0 | ≤0.50 |
| Diameter | Process | Volt | Amps | Shielding Gas | |
| In | mm | ||||
| 0.035 | 0.9 | GMAW | 26-29 | 150-190 | 75%Argon+25%Helium |
| 0.045 | 1.2 | GMAW | 28-32 | 180-220 | 75%Argon+25%Helium |
| 1/16 | 1.6 | GMAW | 29-33 | 200-250 | 75%Argon+25%Helium |
| 0.035 | 0.9 | GTAW | 12-15 | 60-90 | 100% Argon |
| 0.045 | 1.2 | GTAW | 13-16 | 80-110 | 100% Argon |
| 1/16 | 1.6 | GTAW | 14-18 | 90-130 | 100% Argon |
| 3/32 | 2.4 | GTAW | 15-20 | 120-175 | 100% Argon |
| 1/8 | 3.2 | GTAW | 15-20 | 150-220 | 100% Argon |
| 3/32 | 2.4 | SAW | 28-30 | 275-350 | Suitable flux may he usedi |
| 1/8 | 3.2 | SAW | 29-32 | 350-450 | Suitable flux may he usedi |
| 5/32 | 4.0 | SAW | 30-33 | 400-550 | Suitable flux may he usedi |
| Condition | Tensile Strength MPa (ksi) | Yield Strength MPa (ksi) | Elongation% |
| AWS reauirement | 480(70) Typical | Not specified | Not specified |
| Typical results as welded | 530(77) | 360(53) | 34 |
Why ERNiCu-7?
• No Preheat required, maximum interpass temperature 150℃ and no PwHT required
• Dissimilar welding applications include joining alloys to Nickel 200 and copper-nickel alloys-
• Widely used in marine applications because of its good resistance to the corrosive effects of seawater and brackish waters
• Can be used for MIG overlay on steel after a first layer with nickel 208